By adopting precision extrusion system of China GWELL Machinery Co., Ltd., this project is equipped with high precision melt distribution system, screen exchanger, gear pump, melt-blown cloth hanger type Die head, M forming belt, and auxiliary standing electret static treatment and also winding device.

working procedure:

Vacuum feeding -> melt extrusion -> spinneret -> melt fabric forming unit  -> electret treatment -> friction rewinding

widthMachine modeloutput per day

Melt blown fabric can reach PFE 99%

There are you some points which influence the quality of melt blown fabric: 

1. MFI of polymer raw materials

As the best barrier layer of the mask, the melt blown cloth is a very fine material, 

which is made of many crisscross microfibres stacked in random direction. 

Taking PP as an example, the higher MFI is, the finer the wire drawn out during 

melt blown processing, and the better the filtration performance.


2. Hot air injection angle

The hot air injection angle mainly affects the drawing effect and fiber morphology. 

The smaller the angle, the parallel fiber bundle will be formed, which will lead to the poor 

uniformity of the non-woven fabric. If the angle tends to 90 °, a highly dispersed 

and turbulent air flow will be generated, which is conducive to the random distribution 

of fibers on the screen, and the anisotropic property of the final melt blown cloth is good.


3. Screw extrusion speed

Under the condition of constant temperature, the extrusion rate of screw should be kept 

in a certain range: before a certain critical point, the faster the extrusion speed is, the 

higher the quantity of melt blown cloth is, and the greater the strength is; when the

 critical value is exceeded, the strength of melt blown cloth will decrease, especially 

when MFI > 1000, which is more obvious. It may be because the high extrusion rate leads 

to the insufficient draft of wire rod and the serious silk, so the cloth surface is sticky 

The results show that the strength of the melt blown fabric is decreased.


4. Hot air velocity

At the same temperature, screw speed and receiving distance (DCD), the faster the 

hot air speed, the smaller the fiber diameter, the softer the hand feel of the non-woven 

fabric, and the more tangled the fibers, resulting in the denser, smoother and higher 

strength of the fiber mesh.


5. Receiving distance (DCD)

Too long acceptance distance will lead to the decrease of longitudinal and transverse 

strength, bending strength, fluffy handle of non-woven fabric, and the decrease of 

filtration efficiency and filtration resistance in melt blown process.


6. Melt blown die head

Many spinneret die materials on the market are not standard materials. Some low-end 

die steels are used instead. During the use process, there will be some small cracks that 

can not be seen by the eyes. The hole diameter processing is rough and the accuracy is 

poor. It is directly used without polishing. It causes uneven spinneret, poor toughness, 

different spinneret thickness and easy to produce crystallization.